Now it is possible to compile a single precision spectral solver/crystal plasticity by replacing mesh.f90 and prec.f90 with mesh_single.f90 and prec_single.f90.
For the spectral method, just call "make precision=single" instead of "make". Use "make clean" evertime you switch precision
(state < relevant state) or (residuum < relative tolerance * state)
since the relevant value for the state variables depend on their nature and can vary by large scales (e.g. volume fraction: 1e-10, dislocation density: 1e5) it is not possible to set a unique value. instead the constitutive law has to decide what is relevant. therefore, all constitutive laws now read in parameters from the material.config that determine the values for relevantState [@luc: in dislobased law relevant State is for the moment generally set to 1e-200, so no additional parameters necessary in material.config. if you also want this feature, we can still implement it, no big deal]
- added sanity checks in constitutive_nonlocal.f90
- corrected coordinate transformation for backstress calculation in constitutive_nonlocal.f90
- corrected equations for evolution of dipole dislocation densities (athermal annihilation and formation by glide)
# non-greedy memory allocation
# generation of outputConstitutive to allow for script-based T16 extraction
# exchange of phenomenological by more general phenopowerlaw
# lattice is based on slip and twin families which can be treated as individual entities (switched on/off, separate hardening, etc.)
# nicer debugging output
# changed some error/warning codes
# plus potentially some minor additional brushes here and there
Martin Diehl