<materials>
|
|
[TWIP steel FeMnC]
|
|
lattice_structure 1
|
|
Nslip 12
|
|
Ntwin 0
|
|
## Elastic constants
|
|
# Unit in [Pa]
|
|
C11 183.9e9
|
|
C12 101.9e9
|
|
C44 115.4e9
|
|
|
|
## Parameters for phenomenological modeling
|
|
# Unit in [Pa]
|
|
s0_slip 85.0e6
|
|
gdot0_slip 0.001
|
|
n_slip 100.0
|
|
h0 355.0e6
|
|
s_sat 265.0e6
|
|
w0 1.0
|
|
# Self and latent hardening coefficients
|
|
hardening_coefficients 1.0 1.4
|
|
|
|
## Parameters for dislocation-based modeling
|
|
# Burgers vector [m]
|
|
burgers 2.56e-10
|
|
# Activation energy for dislocation glide [J/K] (0.5*G*b^3)
|
|
Qedge 5.5e-19
|
|
# Activation energy for self diffusion [J/K] (gamma-iron)
|
|
Qsd 4.7e-19
|
|
# Vacancy diffusion coeffficent (gamma-iron)
|
|
diff0 4.0e-5
|
|
# Average grain size [m]
|
|
grain_size 2.0e-5
|
|
# Dislocation interaction coefficients
|
|
interaction_coefficients 1.0 2.2 3.0 1.6 3.8 4.5
|
|
|
|
# Initial dislocation density [m]²
|
|
rho0 6.0e12
|
|
# Passing stress adjustment
|
|
c1 0.1
|
|
# Jump width adjustment
|
|
c2 2.0
|
|
# Activation volume adjustment
|
|
c3 1.0
|
|
# Average slip distance adjustment for lock formation
|
|
c4 50.0
|
|
# Average slip distance adjustment when grain boundaries
|
|
c5 1.0
|
|
# Athermal recovery adjustment
|
|
c7 8.0
|
|
# Thermal recovery adjustment (plays no role for me)
|
|
c8 1.0e10
|
|
|
|
## Parameters for mechanical twinning
|
|
# Average twin thickness (stacks) [m]
|
|
stack_size 5.0e-8
|
|
# Total twin volume fraction saturation
|
|
f_sat 1.0
|
|
# Average slip distance adjustment when twin boundaries
|
|
c6
|
|
# Scaling potential nucleation sites
|
|
site_scaling 1.0e-6
|
|
# Scaling the P-K force on the twinning dislocation
|
|
q1 1.0
|
|
# Scaling the resolved shear stress
|
|
q2 1.0
|
|
|
|
|
|
|
|
<textures>
|
|
[cube SX]
|
|
symmetry no /monoclinic /orthorhombic
|
|
Ngrains 10 /2 /4
|
|
#(gauss) phi1 0.0 phi 29.21 phi2 -26.57 scatter 0.0 fraction 1.0
|
|
#(gauss) phi1 0.0 phi 54.74 phi2 -45.0 scatter 0.0 fraction 0.1
|
|
#(gauss) phi1 0.0 phi 45.0 phi2 0.0 scatter 0.0 fraction 0.1
|
|
#(gauss) phi1 0.0 phi 0.0 phi2 0.0 scatter 0.0 fraction 0.1
|
|
#(gauss) phi1 0.0 phi 35.26 phi2 -45.0 scatter 0.0 fraction 0.1
|
|
#(gauss) phi1 0.0 phi 48.19 phi2 -26.57 scatter 0.0 fraction 0.1
|
|
#(gauss) phi1 0.0 phi 26.57 phi2 0.0 scatter 0.0 fraction 0.1
|
|
#(gauss) phi1 0.0 phi 42.03 phi2 -33.69 scatter 0.0 fraction 0.1
|
|
#(gauss) phi1 0.0 phi 40.36 phi2 -11.31 scatter 0.0 fraction 0.1
|
|
#(gauss) phi1 0.0 phi 15.62 phi2 -26.57 scatter 0.0 fraction 0.1
|