<phase>
|
|
#-------------------#
|
|
/echo/
|
|
[Mg]
|
|
plasticity phenopowerlaw
|
|
elasticity hooke
|
|
|
|
(output) resistance_slip
|
|
(output) shearrate_slip
|
|
(output) resolvedstress_slip
|
|
(output) totalshear
|
|
(output) resistance_twin
|
|
(output) shearrate_twin
|
|
(output) resolvedstress_twin
|
|
(output) totalvolfrac
|
|
|
|
lattice_structure hex
|
|
covera_ratio 1.62350 # from Tromans 2011, Elastic Anisotropy of HCP Metal Crystals and Polycrystals
|
|
c11 59.3e9 # - " -
|
|
c33 61.5e9 # - " -
|
|
c44 16.4e9 # - " -
|
|
c12 25.7e9 # - " -
|
|
c13 21.4e9 # - " -
|
|
|
|
# basal prism prism pyr(a) pyr(c+a) pyr(c+a)
|
|
Nslip 3 3 0 6 0 6 # from Agnew et al 2006, Validating a polycrystal model for the elastoplastic response of mg alloy AZ32 using in situ neutron diffraction
|
|
# T1 C1 T2 C2
|
|
Ntwin 6 0 0 6 # - " -
|
|
# basal prism prism pyr(a) pyr(c+a) pyr(c+a)
|
|
tau0_slip 10.0e6 55.0e6 0 60.0e6 0.0 60.0e6 # - " - table 1, pyr(a) set to pyr(c+a)
|
|
tausat_slip 40.0e6 135.0e6 0 150.0e6 0.0 150.0e6 # - " - table 1, pyr(a) set to pyr(c+a)
|
|
# T1 C1 T2 C2
|
|
tau0_twin 40e6 0.0 0.0 60.0e6 # - " - table 1, compressive twin guessed by Steffi, tensile twin modified to match experimental results
|
|
tausat_twin 60e6 0.0 0.0 80.0e6
|
|
|
|
h0_twintwin 50.0e6 # - " - table 1, same range as theta_0
|
|
h0_slipslip 500.0e6 # - " - table 1, same range as theta_0
|
|
h0_twinslip 150.0e6 # guessing
|
|
|
|
interaction_slipslip 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 # just guessing
|
|
interaction_twintwin 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 # - " -
|
|
interaction_sliptwin 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 # - " -
|
|
interaction_twinslip 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 # - " -
|
|
|
|
|
|
|
|
####################################################
|
|
# open for discussion
|
|
####################################################
|
|
atol_resistance 1
|
|
atol_shear 0
|
|
atol_twinfrac 0
|
|
|
|
n_twin 20
|
|
n_slip 20
|
|
|
|
gdot0_twin 0.001
|
|
gdot0_slip 0.001
|
|
|
|
twin_b 0
|
|
twin_c 0
|
|
twin_d 20
|
|
twin_e 20
|
|
|
|
a_slip 2.25
|
|
s_pr 10.0 # push-up factor for slip saturation due to twinning
|