type: phenopowerlaw references: - F. Wang et al., Acta Materialia 80:77-93, 2014, https://doi.org/10.1016/j.actamat.2014.07.048 output: [xi_sl, xi_tw] N_sl: [3, 3, 6, 0, 6] # basal, prism, 1. pyr, -, 2. pyr N_tw: [6, 0, 6] # tension, -, compression xi_0_sl: [10.e+6, 55.e+6, 60.e+6, 0., 60.e+6] xi_inf_sl: [40.e+6, 135.e+6, 150.e+6, 0., 150.e+6] xi_0_tw: [40.e+6, 0., 60.e+6] a_sl: [2.25, 2.25, 2.25, 1, 2.25] dot_gamma_0_sl: [0.001, 0.001, 0.001, 0, 0.001] dot_gamma_0_tw: [0.001, 0, 0.001] n_sl: [20, 20, 20, 1, 20] n_tw: [20, 1, 20] f_sat_sl-tw: [10.0, 10.0, 10.0, 0, 10.0] h_0_sl-sl: [0.5e+9, 0.5e+9, 0.5e+9, 0, 0.5e+9] h_0_tw-tw: [50.0e+6, 0, 50.0e+6] h_0_tw-sl: [0.15e+9, 0, 0.15e+9] h_sl-sl: [+1.0, 1.0, 1.0, 1.0, 1.0, 1.0, 1.0, 1.0, 1.0, 1.0, +1.0, 1.0, 1.0, 1.0, 1.0, 1.0, 1.0, 1.0, 1.0, -1.0, -1.0, -1.0, -1.0, -1.0, -1.0, -1.0, -1.0, -1.0, -1.0, -1.0, -1.0, -1.0, -1.0, -1.0, -1.0, -1.0, -1.0, -1.0, -1.0, -1.0, -1.0, -1.0, -1.0, -1.0, -1.0, -1.0, 1.0, 1.0, 1.0, 1.0, +1.0, 1.0, -1.0, -1.0, -1.0, -1.0, 1.0, 1.0, 1.0, 1.0, -1.0, -1.0, -1.0, -1.0, 1.0, 1.0, 1.0, 1.0, 1.0] # unused entries are indicated by -1.0 h_tw-tw: [+1.0, 1.0, -1.0, -1.0, -1.0, -1.0, 1.0, -1.0, 1.0, 1.0, -1.0, 1.0] # unused entries are indicated by -1.0 h_tw-sl: [1.0, -1.0, 1.0, -1.0, 1.0, -1.0, 1.0, -1.0, 1.0, -1.0, 1.0, -1.0, -1.0, -1.0, -1.0, -1.0, +1.0, -1.0, 1.0, -1.0] # unused entries are indicated by -1.0 h_sl-tw: [1.0, -1.0, 1.0, -1.0, 1.0, -1.0, 1.0, -1.0, 1.0, -1.0, 1.0, -1.0, -1.0, -1.0, -1.0, -1.0, +1.0, -1.0, 1.0] # unused entries are indicated by -1.0