fe70a82d6d
!!!!! IMPORTANT !!!!!
...
All subroutines were committed at once:
- constitutive_pheno works
- constitutive_dislo without twinning also works
This release should serve as reference
2007-12-14 13:36:04 +00:00
08a1c38c73
Finalizing the implementation of deformation twinning in constitutive_dislo.f90
...
Assume to be ready to use
2007-12-10 12:55:43 +00:00
d0f6c81d66
constitutive_Microstructure() computes now twin "plop" volumes from the given microstructure.
...
Mattex.dat has 2 parameters for deformation twinning:
- average grain size
- average twin stack thickness
2007-12-07 15:12:43 +00:00
b69aa2b112
Construction of the elasticity matrices for rotated/twin regions.
...
Definition of constitutive_Ntwin and constitutive_MaxNtwin
2007-12-07 13:59:15 +00:00
3c0d51542e
Changed to SI conformity. Mattex file changed bg->burgers
2007-11-15 17:04:30 +00:00
ee81ae29df
Update of mattex file (monoclinic-2)
2007-10-16 16:59:55 +00:00
296f09d225
Checked computation of hardening matrix
...
In case of constitutive_pheno.f90, the computation can be optimized.
Mattex file slightly modified
2007-10-16 12:20:58 +00:00
ad470f6ee0
Added explanations and comments in mattex file
...
The dislocation based constitutive subroutine can be only use for fcc crystal !!!!
The constitutive equations are different for bcc and hcp.
2007-10-16 12:11:58 +00:00
4a70b4dbbc
Added a possible example of mattex file
...
Some syntax corrections
2007-10-16 11:50:51 +00:00
Luc Hantcherli