removed unused parameters. Why was shearbanding on in for HMs TWIP steel?

examples/ConfigFiles/Phase_Dislotwin_TWIP-Steel-FeMnC.config

@@ -50,7 +50,7 @@ interactionSlipSlip 0.122 0.122 0.625 0.07 0.137 0.122 # Interaction coefficient
 
 ### Shearband parameters ###
 shearbandresistance 180e6
-shearbandvelocity   1e-4            # set to zero to turn shear banding of
+shearbandvelocity   0e-4            # set to zero to turn shear banding of
 QedgePerSbSystem    3.7e-19         # Activation energy for shear banding [J]
 p_shearband         1.0             # p-exponent in glide velocity
 q_shearband         1.0             # q-exponent in glide velocity

examples/ConfigFiles/Phase_Phenopowerlaw_BCC-Ferrite.config

@@ -18,8 +18,5 @@ tau0_slip                95.e6  97.e6           # per family, optimization long
 tausat_slip             222.e6 412.7e6          # per family, optimization long simplex 109
 h0_slipslip             1000.0e6
 interaction_slipslip    1 1 1.4 1.4 1.4 1.4
-interaction_sliptwin    1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1
-interaction_twinslip    1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1
-interaction_twintwin    1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1
 w0_slip                 2.0
 (output) totalshear

examples/ConfigFiles/Phase_Phenopowerlaw_BCC-Martensite.config

@@ -18,8 +18,5 @@ tau0_slip               405.8e6  456.7e6        # per family
 tausat_slip             872.9e6  971.2e6        # per family
 h0_slipslip             563.0e9
 interaction_slipslip    1 1 1.4 1.4 1.4 1.4
-interaction_sliptwin    1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1
-interaction_twinslip    1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1
-interaction_twintwin    1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1
 w0_slip                 2.0
 (output) totalshear

examples/ConfigFiles/Phase_Phenopowerlaw_Gold.config

@@ -35,18 +35,7 @@ tausat_slip             53.00e6                # per family
 a_slip                  1.0
 gdot0_twin              0.001
 n_twin                  20
-tau0_twin               0                     # per family
-s_pr                    0                     # push-up factor for slip saturation due to twinning
-twin_b                  0
-twin_c                  0
-twin_d                  0
-twin_e                  0
 h0_slipslip             75e6
-h0_twinslip             0
-h0_twintwin             0
 interaction_slipslip    1 1 1.4 1.4 1.4 1.4
-interaction_sliptwin    1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1
-interaction_twinslip    1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1
-interaction_twintwin    1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 
 atol_resistance         1
 

examples/ConfigFiles/Phase_Phenopowerlaw_multiField.config

@@ -29,18 +29,8 @@ a_slip                  2.25
 gdot0_twin              0.001
 n_twin                  20
 tau0_twin               31e6                # per family
-s_pr                    0                     # push-up factor for slip saturation due to twinning
-twin_b                  0
-twin_c                  0
-twin_d                  0
-twin_e                  0
 h0_slipslip             75e6
-h0_twinslip             0
-h0_twintwin             0
 interaction_slipslip    1 1 1.4 1.4 1.4 1.4
-interaction_sliptwin    1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1
-interaction_twinslip    1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1
-interaction_twintwin    1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 
 atol_resistance         1
 
 (stiffness_degradation) damage