will not work without populate grains

This commit is contained in:
Martin Diehl 2018-10-14 21:41:32 +02:00
parent 1839228add
commit d662507eb8
6 changed files with 0 additions and 2957 deletions

View File

@ -405,14 +405,6 @@ SpectralExample:
only: only:
- development - development
AbaqusExample:
stage: example
script:
- module load $IntelCompiler16_4 $Abaqus
- Abaqus_example/test.py
only:
- development
################################################################################################### ###################################################################################################
SpectralRuntime: SpectralRuntime:
stage: performance stage: performance

File diff suppressed because it is too large Load Diff

View File

@ -1,23 +0,0 @@
# Save by m.diehl on 2017_12_06-18.38.26; build 2017 2016_09_27-23.54.59 126836
from abaqus import *
upgradeMdb(
'/nethome/storage/raid4/m.diehl/DAMASK/examples/AbaqusStandard/SX_PX_compression-6.9-1.cae'
,
'/nethome/storage/raid4/m.diehl/DAMASK/examples/AbaqusStandard/SX_PX_compression.cae')
# Save by m.diehl on 2017_12_06-18.38.26; build 2017 2016_09_27-23.54.59 126836
from part import *
from material import *
from section import *
from assembly import *
from step import *
from interaction import *
from load import *
from mesh import *
from optimization import *
from job import *
from sketch import *
from visualization import *
from connectorBehavior import *
mdb.jobs['Job_sx-px'].setValues(description='compression', userSubroutine=
'$HOME/DAMASK/src/DAMASK_abaqus_std.f')
# Save by m.diehl on 2017_12_06-18.39.44; build 2017 2016_09_27-23.54.59 126836

View File

@ -1,93 +0,0 @@
#-------------------#
<homogenization>
#-------------------#
[dummy]
mech none
[poly]
mech isostrain
Nconstituents 10
#-------------------#
<microstructure>
#-------------------#
[Aluminum_001]
crystallite 1
(constituent) phase 1 texture 1 fraction 1.0
[Aluminum_10]
crystallite 1
(constituent) phase 1 texture 2 fraction 1.0
#-------------------#
<crystallite>
#-------------------#
[orientation]
(output) eulerangles
(output) grainrotation # deviation from initial orientation as axis (1-3) and angle in degree (4)
#-------------------#
<phase>
#-------------------#
[Aluminum_phenopowerlaw]
# slip only
elasticity hooke
plasticity phenopowerlaw
(output) resistance_slip
(output) shearrate_slip
(output) resolvedstress_slip
(output) totalshear
(output) resistance_twin
(output) shearrate_twin
(output) resolvedstress_twin
(output) totalvolfrac
lattice_structure fcc
Nslip 12
Ntwin 0
c11 106.75e9
c12 60.41e9
c44 28.34e9
gdot0_slip 0.001
n_slip 20
tau0_slip 31e6 # per family
tausat_slip 63e6 # per family
a_slip 2.25
gdot0_twin 0.001
n_twin 20
tau0_twin 31e6 # per family
s_pr 0 # push-up factor for slip saturation due to twinning
twin_b 0
twin_c 0
twin_d 0
twin_e 0
h0_slipslip 75e6
h0_sliptwin 0
h0_twinslip 0
h0_twintwin 0
interaction_slipslip 1 1 1.4 1.4 1.4 1.4
interaction_sliptwin 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1
interaction_twinslip 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1
interaction_twintwin 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1
atol_resistance 1
#-------------------#
<texture>
#-------------------#
[001]
(gauss) phi1 0.000 Phi 45.000 phi2 0.000 scatter 0.000 fraction 1.000
[random]

View File

@ -1 +0,0 @@
fixed_seed 1697667030