combined single crystal (SX) and polycrystal (PX) compression samples

examples/SX_PX_compression/SX_PX_compression.jnl

@@ -0,0 +1 @@
+# Save by abaqususer on Thu May 12 10:22:10 2011

examples/SX_PX_compression/material.config

@@ -0,0 +1,97 @@
+#####################
+# $Id: material.config 673 2010-10-26 13:16:37Z MPIE\c.kords $
+#####################
+
+#-------------------#
+<homogenization>
+#-------------------#
+
+[SX]
+type	isostrain
+Ngrains	1
+
+[poly]
+type	isostrain
+Ngrains	10
+
+
+
+#-------------------#
+<microstructure>
+#-------------------#
+
+
+[Aluminum_001]
+crystallite	1
+(constituent)	phase 1	texture	1	fraction	1.0
+
+[Aluminum_10]
+crystallite	1
+(constituent)	phase 1	texture	2	fraction	1.0
+
+#-------------------#
+<crystallite>
+#-------------------#
+
+[all]
+(output) eulerangles
+(output) grainrotation  # deviation from initial orientation as axis (1-3) and angle in degree (4)
+
+#-------------------#
+<phase>
+#-------------------#
+
+
+[Aluminum_phenopowerlaw]
+# slip only
+constitution            phenopowerlaw
+
+(output)                resistance_slip
+(output)                shearrate_slip
+(output)                resolvedstress_slip
+(output)                totalshear
+(output)                resistance_twin
+(output)                shearrate_twin
+(output)                resolvedstress_twin
+(output)                totalvolfrac
+
+lattice_structure       fcc
+Nslip                   12  0  0  0              # per family
+Ntwin                    0  0  0  0              # per family
+
+c11                     106.75e9
+c12                     60.41e9
+c44                     28.34e9
+
+gdot0_slip              0.001
+n_slip                  20
+tau0_slip                 31e6                # per family
+tausat_slip               63e6               # per family
+w0_slip                 2.25
+gdot0_twin              0.001
+n_twin                  20
+tau0_twin                 31e6               # per family
+s_pr                    0                        # push-up factor for slip saturation due to twinning
+twin_b                  0
+twin_c                  0
+twin_d                  0
+twin_e                  0
+h0_slipslip             75e6
+h0_sliptwin             0
+h0_twinslip             0
+h0_twintwin             0
+interaction_slipslip    1 1 1.4 1.4 1.4 1.4
+interaction_sliptwin    1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1
+interaction_twinslip    1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1
+interaction_twintwin    1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 
+atol_resistance         1
+
+
+#-------------------#
+<texture>
+#-------------------#
+
+[001]
+(gauss)		phi1	0.000	Phi	45.000	phi2	0.000	scatter	0.000	fraction	1.000
+
+[random]