[Tungsten]
|
||
|
|
elasticity hooke
|
||
|
|
plasticity disloucla
|
||
|
|
|
||
|
|
(output) edge_density
|
||
|
|
(output) dipole_density
|
||
|
|
(output) shear_rate_slip
|
||
|
|
(output) accumulated_shear_slip
|
||
|
|
(output) mfp_slip
|
||
|
|
(output) resolved_stress_slip
|
||
|
|
(output) threshold_stress_slip
|
||
|
|
(output) twin_fraction
|
||
|
|
(output) shear_rate_twin
|
||
|
|
(output) accumulated_shear_twin
|
||
|
|
(output) mfp_twin
|
||
|
|
(output) resolved_stress_twin
|
||
|
|
(output) threshold_stress_twin
|
||
|
|
|
||
|
|
### Material parameters ###
|
||
|
|
lattice_structure bcc
|
||
|
|
C11 523.0e9 # From Marinica et al. Journal of Physics: Condensed Matter(2013)
|
||
|
|
C12 202.0e9
|
||
|
|
C44 161.0e9
|
||
|
|
|
||
|
|
grainsize 2.7e-5 # Average grain size [m] 2.0e-5
|
||
|
|
SolidSolutionStrength 0.0 # Strength due to elements in solid solution
|
||
|
|
|
||
|
|
### Dislocation glide parameters ###
|
||
|
|
#per family
|
||
|
|
Nslip 12 0
|
||
|
|
slipburgers 2.72e-10 # Burgers vector of slip system [m]
|
||
|
|
rhoedge0 1.0e12 # Initial edge dislocation density [m/m**3] 1.0e12
|
||
|
|
rhoedgedip0 1.0 # Initial edged dipole dislocation density [m/m**3]
|
||
|
|
Qedge 2.725e-19 # Activation energy for dislocation glide [J]
|
||
|
|
v0 3693.4 # Initial glide velocity [m/s] 1.0e-4 (kmC 3693.4 ; 755.59)
|
||
|
|
p_slip 0.86 # p-exponent in glide velocity
|
||
|
|
q_slip 1.69 # q-exponent in glide velocity
|
||
|
|
tau_peierls 2.03e9 # peierls stress [Pa]
|
||
|
|
|
||
|
|
#mobility law
|
||
|
|
kink_height 2.567e-10 # kink height sqrt(6)/3*lattice_parameter [m]
|
||
|
|
omega 9.1e11 # attemp frequency (from kMC paper) [s^(-1)]
|
||
|
|
kink_width 29.95e-10 # kink pair width ~ 11 b (kMC paper) [m]
|
||
|
|
dislolength 78.0e-10 # dislocation length (ideally lambda) [m] initial value 25b
|
||
|
|
friction_coeff 8.3e-5 # friction coeff. B (kMC) [Pa*s]
|
||
|
|
#
|
||
|
|
|
||
|
|
#hardening
|
||
|
|
dipoleformationfactor 0 # to have hardening due to dipole formation off
|
||
|
|
CLambdaSlip 10.0 # Adj. parameter controlling dislocation mean free path
|
||
|
|
D0 4.0e-5 # Vacancy diffusion prefactor [m**2/s]
|
||
|
|
Qsd 4.5e-19 # Activation energy for climb [J]
|
||
|
|
Catomicvolume 1.0 # Adj. parameter controlling the atomic volume [in b]
|
||
|
|
Cedgedipmindistance 1.0 # Adj. parameter controlling the minimum dipole distance [in b]
|
||
|
|
interaction_slipslip 0.0625 0.0625 0.72 0.05 0.09 0.06 # Queyreau
|
||
|
|
#nonschmid_coefficients 0 0.56 0.75 0 0 0 #??????????????
|