DAMASK_EICMD/examples/config/phase/mechanical/eigen/thermalexpansion_AISI304.yaml

type: thermalexpansion

references:
  - R.H. Bogaard et al.,
    Thermochimica Acta 218:373-393, 1993,
    https://doi.org/10.1016/0040-6031(93)80437-F,
    fit to Fig. 6 (T_min=100K, T_max=1200K)

Alpha_11: 14.9e-6
Alpha_11,T: 1.838e-08
Alpha_11,T^2: -2.028e-11
Alpha_11,T^3: 9.173e-15

T_ref: 293.15
new material parameters - austenitic steel AISI304 - SAE1050 after quenching to martensite I don't know how the old set of elastic constants for martenstite (originally coming from 10.1088/0965-0393/23/4/045005) was derived, but it is hard to believe that the elastic behavior can be that strongly modified by a heat treatment. 2021-12-27 13:50:15 +05:30			`type: thermalexpansion`
polishing 2022-02-12 23:11:59 +05:30
new material parameters - austenitic steel AISI304 - SAE1050 after quenching to martensite I don't know how the old set of elastic constants for martenstite (originally coming from 10.1088/0965-0393/23/4/045005) was derived, but it is hard to believe that the elastic behavior can be that strongly modified by a heat treatment. 2021-12-27 13:50:15 +05:30			`references:`
polishing 2022-02-12 23:11:59 +05:30			`- R.H. Bogaard et al.,`
			`Thermochimica Acta 218:373-393, 1993,`
adjustments and improved documentation 2022-02-13 01:56:42 +05:30			`https://doi.org/10.1016/0040-6031(93)80437-F,`
re-fit using correct scaling code is in 'parameters' repository 2023-01-08 15:27:06 +05:30			`fit to Fig. 6 (T_min=100K, T_max=1200K)`
polishing 2022-02-12 23:11:59 +05:30
re-fit using correct scaling code is in 'parameters' repository 2023-01-08 15:27:06 +05:30			`Alpha_11: 14.9e-6`
			`Alpha_11,T: 1.838e-08`
			`Alpha_11,T^2: -2.028e-11`
			`Alpha_11,T^3: 9.173e-15`
adjustments and improved documentation 2022-02-13 01:56:42 +05:30
have EOL and EOF 2023-01-08 19:02:13 +05:30			`T_ref: 293.15`