DAMASK_EICMD/examples/config/phase/mechanical/elastic/Hooke_AISI304.yaml

type: Hooke

references:
  - H.M. Ledbetter,
    physica status solidi (a) 85(1):89-96, 1984,
    https://doi.org/10.1002/pssa.2210850111

C_11: 204.6e+9
C_12: 137.7e+9
C_44: 126.2e+9
new material parameters - austenitic steel AISI304 - SAE1050 after quenching to martensite I don't know how the old set of elastic constants for martenstite (originally coming from 10.1088/0965-0393/23/4/045005) was derived, but it is hard to believe that the elastic behavior can be that strongly modified by a heat treatment. 2021-12-27 13:50:15 +05:30			`type: Hooke`
polishing 2022-02-12 23:11:59 +05:30
new material parameters - austenitic steel AISI304 - SAE1050 after quenching to martensite I don't know how the old set of elastic constants for martenstite (originally coming from 10.1088/0965-0393/23/4/045005) was derived, but it is hard to believe that the elastic behavior can be that strongly modified by a heat treatment. 2021-12-27 13:50:15 +05:30			`references:`
polishing 2022-02-12 23:11:59 +05:30			`- H.M. Ledbetter,`
			`physica status solidi (a) 85(1):89-96, 1984,`
new material parameters - austenitic steel AISI304 - SAE1050 after quenching to martensite I don't know how the old set of elastic constants for martenstite (originally coming from 10.1088/0965-0393/23/4/045005) was derived, but it is hard to believe that the elastic behavior can be that strongly modified by a heat treatment. 2021-12-27 13:50:15 +05:30			`https://doi.org/10.1002/pssa.2210850111`
polishing 2022-02-12 23:11:59 +05:30
new material parameters - austenitic steel AISI304 - SAE1050 after quenching to martensite I don't know how the old set of elastic constants for martenstite (originally coming from 10.1088/0965-0393/23/4/045005) was derived, but it is hard to believe that the elastic behavior can be that strongly modified by a heat treatment. 2021-12-27 13:50:15 +05:30			`C_11: 204.6e+9`
			`C_12: 137.7e+9`
			`C_44: 126.2e+9`